Tiny MoOₓ clusters on TiO₂ nanosheets boost selectivity in photocatalytic methane oxidation

Researchers from the Innovation Academy for Precision Measurement Science and Technology (APM) of the Chinese Academy of Sciences has discovered that anchoring subnanometric MoO_x clusters onto TiO₂ nanosheets can effectively suppress the formation of CO₂ during methane oxidation, significantly enhancing the selectivity for oxygenated organic products.

This discovery sheds light on the activity and mechanism of photocatalytic selective oxidation of methane. The research is published in Nature Communications.

Methane (CH₄), abundant but chemically inert, presents challenges for direct conversion into high-value products like methanol and formaldehyde. Traditional thermocatalytic methods require harsh conditions and often suffer from low selectivity, leading to over-oxidation.

Photocatalysis, driven by solar energy, offers a greener alternative but improving both activity and selectivity remains difficult.

While noble metal cocatalysts such as gold improve performance, their high cost limits practical application. Hence, non-noble metal promoters like nickel and cobalt have garnered interest, yet balancing conversion rate and selectivity remains elusive.

In this study, the researchers developed a TiO₂-based photocatalyst decorated with ultrasmall (0.6 nm) MoO_x clusters. They achieved an efficient photocatalytic oxidation reaction of methane.

The catalyst with a 0.5% MoO_x loading exhibited the optimal catalytic activity, achieving an organic oxygenate yield of 3.8 mmol/g within two hours, with selectivity approaching nearly 100%. It exhibited an apparent quantum yield of 13.3% at 365 nm and maintained stable high selectivity (>95%) over 1,800 minutes of continuous reaction, demonstrating excellent durability.

In situ Electron Paramagnetic Resonance (EPR) and Nuclear Magnetic Resonance (NMR) analyses revealed that MoO_x clusters activate O₂ to form surface-active species (Mo−OO and Mo−OOH), which facilitate the activation of methane’s carbon-hydrogen bonds to form reaction intermediates (Mo-CH₂). This effectively inhibits the formation of hydroxyl radicals (•OH) and superoxide radicals (O₂•−), thereby reducing the over-oxidation of products.

Moreover, photogenerated electrons reduce Mo species that, in the presence of water, facilitate formaldehyde desorption from the catalyst surface, preventing further oxidation.

This study provides new insights for designing efficient non-noble metal catalysts, advancing the practical application of methane conversion technology.